ISO 12154:2014 Determination of density by volumetric displacement - Skeleton density by gas pycnometry
来源: | From: Gold APP Instruments | Published Date: 2023-02-02 | 788 Time(s) of View | 分享到:
The true solid state density of a material is defined as the ratio of the mass to the volume occupied by that mass. Therefore, the contribution to the volume made by pores or internal voids and also interparticle voids (in the case of granulated or highly dispersed samples) shall be subtracted when calculating the true density.

Introduction


The true solid state density of a material is defined as the ratio of the mass to the volume occupied by that mass. Therefore, the contribution to the volume made by pores or internal voids and also interparticle voids (in the case of granulated or highly dispersed samples) shall be subtracted when calculating the true density.


If the material has no porosity, the true density can be measured by displacement of any fluid in which the solid remains inert. The accuracy of the method is limited by the accuracy with which the fluid volume can be determined. Usually, however, the pores, cracks, or crevices of the material will not easily be completely penetrated by a displaced liquid. In these instances, the true density can be measured by using a gas as the displaced fluid if the material does not contain closed pores, which cannot be penetrated by the analysis gas. Therefore, the density experimentally determined by gas pycnometry generally is the so called skeleton density of the material which equals the true solid state density only for samples without closed pores.


Apparatus used to measure solid volumes are often referred to as pyknometers or pycnometers after the Greek “pyknos”, meaning thick or dense. With gas pycnometry, materials of irregular shape can be analysed.


Once the volume of solid skeleton of the sample and the sample mass have been determined, the skeleton density is readily calculated.


1   Scope

This International Standard specifies a method for rapid and efficient determination of the skeleton density of solid material samples of regular or irregular shape, whether powdered or in one piece, by means of a gas displacement pycnometer.


2   Normative references

The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.

ISO 14488, Particulate materials — Sampling and sample splitting for the determination of particulate properties

ISO 9277, Determination of the specific surface area of solids by gas adsorption — BET method

ISO 15901-3, Pore size distribution and porosity of solid materials by mercury porosimetry and gas adsorption — Part 3: Analysis of micropores by gas adsorption


3   Terms and definitions

For the purposes of this document, the following terms and definitions apply.

3.1 density

ratio of the mass of a certain amount of a sample to the volume occupied by that mass

3.2 true solid state density

ratio of the sample mass to the volume of the compact solid skeleton of the sample which excludes the volume of open and closed pores or internal voids and also interparticle voids as in the case of granulated or highly dispersed samples

3.3 skeleton density

ratio between sample mass and the volume of the sample including the volume of closed pores (if present) but excluding the volumes of open pores as well as that of void spaces between particles within the bulk sample

3.4 closed pore

pore totally enclosed by its walls and hence not interconnecting with other pores and not accessible to fluids

3.5 open pore

pore not totally enclosed by its walls and open to the surface either directly or by interconnecting with other pores and therefore accessible to fluids

3.6 gauge pressure sensor

because gauge pressure is defined relative to atmospheric conditions, the signal or reading of a gauge pressure sensor is the total pressure minus atmospheric pressure

3.7 absolute pressure sensor

absolute pressure sensor measures the pressure relative to an absolute vacuum that means the reference is full vacuum (zero pressure)


Principle of the method

The skeleton density will be determined volumetrically in a gas expansion pycnometer. This technique is based on the displacement of a volume of gas by the solid space. The measurement is performed by expanding gas from one chamber to another (see Figure 1) under isothermal conditions. First, the weight of the dry sample is to be determined and the sample loaded into the sample chamber. The sample chamber then is pressurised to a set value when using the experimental configuration 1 of Figure 1. In a further step, the analysis gas will be expanded into a second chamber, the reference volume. The equilibrated pressures for both steps will be recorded by the instrument. Density is calculated using these values.


For gas pycnometers according to the experimental configuration 2 of Figure 1, the first step consists in pressurising the reference chamber to a set value followed by the expansion into the sample chamber having a lower initial pressure than the set value. It is important for both experimental pycnometer configurations, that every chamber of the pycnometer is at the same pressure p0 prior to starting the analysis steps (see Clause 6) Furthermore, all parts of the pycnometer must have the same controlled temperature.


The analysis gas of sufficient purity (see Subclause 6.1) must be nonreactive and behave as ideally as possible. Therefore, helium is used for most applications. Another reason for the preferred use of helium as the analysis gas for gas pycnometry is that it is able to penetrate even the smallest pores or cracks of a material.


NOTE 1 Because of its pronounced ability to permeate thin inner walls of samples with closed cells, helium may cause difficulties if permeable samples are to be analyzed. Therefore, as described in Annex A.6, gas pycnometric measurements using helium may be erroneous in the case of organic samples like cellulose and celluar polymers with low density. For density measurements of those samples, the use of alternative inert gases such as nitrogen, argon, or sulfur hexafluoride but also dry air is recommended.


NOTE 2 If the sample contains no closed pores, then the volume measured by gas pycnometry is the true volume. To test the presence of closed pores, after a first density determination the sample can be powdered revealing any possible closed pores accessible to the test gas. An increased density value of the ground sample material indicates closed pores in the original sample.


Apparatus

  • Gas expansion pycnometer with fixed-volume sample chamber (see Figure 1)

  • Calibrated reference sample (in general calibration spheres made of stainless steel with known traceable volume)

  • Analysis gas, in general helium (see Clause 5) with a minimum purity of 99,996 % (by volume)

  • Analytical balance

  • Drying oven for pre-treatment of samples preferably with the option of purging during heating or heating in a vacuum

ISO 12154:2014 Determination of density by volumetric displacement - Skeleton density by gas pycnometry

*Contact us (sales@goldapp.com.cn) to get this downloaded PDF*